Hydrophobic SIO2/Al2O3 80 Zeolite Molecular Sieve

 

Hydrophobic ZSM-5 Zeolite Molecular Sieve For Petrochemical Processing Industries

 

Acid resistance

ZSM-5 zeolite has good acid resistance, it is resistant to various acids except hydrofluoric acid.

Mole Ratio: 15-1000
Nominal Cation Form: Ammonium/Hydrogen

Products	SiO2/Al2O3Mole Ratio	Nominal Cation Form	Na2O Weight %	Surface Area, m2/g
QD 01	25	Sodium/Hydrogen	0.05	450
QD O2	30	Sodium/Hydrogen	0.05	450
QD 03	50	Sodium/Hydrogen	0.05	450
QD 04	80	Sodium/Hydrogen	0.05	450
QD 05	280	Sodium/Hydrogen	0.05	450

 

 

 

 

 

 

 

 

Na₂O Weight %: 0.05
Surface Area, m²/g: 450

Description:

ZSM-5 zeolite properties

 

Thermal stability

High thermal stability of ZSM-5 zeolite. This is caused by a skeleton in a stable five-membered ring structure and a high silica to alumina ratio. For example, the sample calcined at 850 ℃ After 2 hours, the crystal structure unchanged. Even can withstand high temperature of 1100 ℃. So far, ZSM-5 zeolites are known to one of the highest qualitative hot temperature. Therefore, it is used in high-temperature process is particularly suitable. For example, use it as a hydrocarbon cracking catalyst, regeneration of the catalyst can withstand passage of time.

 

Steam stability

The studies have shown that when other zeolites by steam and hot water, and their general structure is destroyed, leading to irreversible deactivation. The Mobil company with ZSM-5 as the conversion of methanol (water is one of the major product) catalyst. This suggests that ZSM-5 to water vapor with good stability. 540 ℃ lower partial pressure of 22mmHg steaming column and HY zeolite HZSM-5 after 24 hours, a crystallinity of HZSM-5 and about 70 percent of fresh catalyst, but under the same conditions, HY zeolite skeleton almost completely damage.

 

Hydrophobic

ZSM-5 having a high silica to alumina ratio, the smaller the surface charge density. The water molecule is polar, so you will not ZSM-5 is adsorbed. Although water molecules smaller than the diameter of n-hexane, but the amount of adsorption of n-hexane ZSM-5 is generally greater than water.

 

Easy to coke

ZSM-5 V-shaped aperture effective, pore size and bending, preventing a large condensate formation and accumulation. Meanwhile, ZSM-5 framework is no greater than the bore of the cavity (cage) exist, so limiting the formation of large molecules from the secondary condensation reactions. So that the possibility of ZSM-5 catalyst coke is reduced. ZSM-5 for an alkyl aromatics into the tunnel barrier is formed, and thus the reaction process it can not continue to react in smaller pores, the final condensation formed coke. ZSM-5 so much slower than the rate of coke deposition and Y-type mordenite, difference of almost two orders of magnitude. Capacity of ZSM-5 zeolite carbon content is higher.

 

Excellent shape-selective selectivity

Zeolite molecular sieve as catalyst, only smaller than the hole crystal molecules can catalyze the reaction out of control pore size crystalline zeolite suffering zeolite catalyst size and shape of reactant and product molecules showed great selectivity. Pore ​​system of ZSM-5 zeolite having a 10-MR constituted medium size orifice diameter, it has a good shape-selective selectivity.

Our zeoite and catalyst factory are in follow.

The fixed-bed catalyst production project covers an area of about 5,000 square meters and a building area of 2,000 square meters. It is fully equipped with public works and has more than 40 sets of catalyst production equipment. It has a complete fixed-bed catalyst production system, and the production units that can be carried out mainly include: pretreatment of catalyst raw powder, impregnation, molding, drying/roasting, screening and environmental protection treatment, etc., which can meet the production of various fixed-bed catalysts.